Aluminum bronze is the highest strength standard copper based alloy. Concast produces C95400, C95500 and C95900 in standard sizes of rounds, tubes and rectangles. Aluminum in conjunction with iron and nickel in C95500 acts as a strengthener in these alloys. All of the aluminum bronzes can be heat treated, further increasing tensile strengths.

Info

Product Description: Aluminum Bronze
Solids: 1/2" to 9" O.D.
Tubes: 1 1/8" to 9" O.D.
Rectangles: Up to 15"
Standard Lengths: 144"
Shape/Form: semi-finished, mill stock or near-net shapes, anode, bar stock, billet/bloom, squares, hex, plate, profile or structural shape, flats/rectangular bar

Typical Uses

Industrial: bearings, spur gears, gears, pickling baskets, worms, valve components, bushings, pickling hooks

Note: Also available in a heat-treated condition.

Similar or Equivalent Specification

CDA ASTM Asarcon SAE AMS Federal Military Other
C95410 B505
B505M
           

Chemical Composition

Cu% Fe% Ni%1 Al% Mn%
Chemical Composition according to ASTM B505/B505M-18

1Ni value includes Co.
Note: Cu + Sum of Named Elements, 99.5% min. Single values, unless otherwise noted, represent maximums.
83.00
min
3.00-
5.00
1.50-
2.50
10.00-
11.50
 
0.50

Machinability

Copper Alloy UNS No. Machinability Rating Density (lb/cu in at 68 °F)
C95410 60 0.269

Mechanical Properties

Mechanical Properties according to ASTM B505/B505M-18
Tensile Strength, min Yield Strength, at .5% Extension Under Load, min Elongation, in 2 in. or 50 mm min Brinell Hardness (3000 kg load) Remarks
ksi MPa ksi MPa % typical BHN  
85 586 32 221 12 170  

Physical Properties

  US Customary Metric
Physical Properties provided by CDA
Melting Point - Liquidus 1900 °F 1038 °C
Melting Point - Solidus 1880 °F 1027 °C
Density 0.269 lb/in3 at 68 °F 7.45 gm/cm3 at 20 °C
Specific Gravity 7.45 7.45
Electrical Conductivity 13% IACS at 68 °F 0.075 MegaSiemens/cm at 20 °C
Thermal Conductivity 33.9 Btu/sq ft/ft hr/°F at 68 °F 58.7 W/m at 20 °C
Coefficient of Thermal Expansion 68-572 9 · 10-6 per °F (68-572 °F) 15.5 · 10-6 per °C (20-300 °C)
Specific Heat Capacity 0.1 Btu/lb/°F at 68 °F 419 J/kg at 293 °C
Modulus of Elasticity in Tension 15500 ksi 107000 MPa

Fabrication Properties

Fabrication Properties provided by CDA
Joining Technique Suitability
Soldering Good
Brazing Good
Oxyacetylene Welding Not Recommended
Gas Shielded Arc Welding Good
Coated Metal Arc Welding Good

Thermal Properties

Thermal Properties provided by CDA
Treatment Temp./Time - US Temp./Time - SI
Stress Temperature 600 316
Solution Minimum 1600 872
Solution Maximum 1675 914
Solution Time 1  
Solution Medium Water  
Precipitation Value    
Precipitation Time    
Precipitation Medium    
Annealing Minimum 1150 622
Annealing Maximum 1225 663
Annealing Time 1  
Hot Works Minimum    
Hot Works Maximum    