Product Description: Cartridge Brass, 70%
Tempers: H01 Quarter-Hard, H02 Half-Hard, H04 Hard
Solids: 3⁄8" to 2 1/2" OD
Hex: 3⁄8" to 2" OD
Rectangles: Consult Mill
Standard Lengths: 144"

Typical Uses

Architecture: grillwork
Automotive: odometer contacts, heater cores, thermostats, electrical connectors, radiator cores, radiator tube, radiator tanks, tanks
Builders Hardware: locks, push plates, finish hardware, kick plates, decorative hardware, door knobs, hinges
Consumer: snaps, planters, fireplace screens, etched articles, bird cages, coinage, chain links, pen/pencil inserts and clips, syringe parts, watch parts, costume jewelry, buttons, shells, electrical sockets, lamps
Electrical: terminal connectors, flashlight shells, lamp fixtures, reflectors, screw shells
Fasteners: pins, rivets, fasteners, grommets, eyelets, screws
Industrial: air pressure conveyer systems, sound proofi ng equipment, springs, chain, bead chain, tubing for instruments and machines, heat exchangers, pump cylinders, wire screens, pumps, liners, power cylinders
Ordance ammunition cartridge cases, mechanical housings for lighters, mechanical housings for ammunition, ammunition
Other stencils, washers
Plumbing: fittings, bathroom fixtures, plumbing accessories, faucet escutcheons, traps, plumbing brass goods

Similar or Equivalent Specification

CDA ASTM ASARCON SAE AMS Federal Military Other
C26000 B927
B927M		   J461
J463		        

Chemical Composition (according to ASTM B927/B927M-13)

Alloy Cu% Sn% Pb% Zn% Fe%
Note: Cu + Sum of Named Elements, 99.7% min. Single values represent maximums.
C26000 68.50-
71.50		  
0.05		  
0.07		 Remainder  
0.05

Machinability

Alloy Machinability Rating Density (lb/cu in.)
C26000 30 0.308

Mechanical Properties (according to ASTM B927/B927M-13)

H01 Quarter-Hard Temper

SIZE RANGE: UNDER ½" DIAMETER
Tensile Strength (min) Yield Strength, at .5% extension under load min Elongation, in 2 in. or 50 mm min Brinell Hardness   Remarks
Ksi MPa Ksi MPa % typical BHN  
50 345 30 205 20    
SIZE RANGE: OVER ½" TO 1" INCLUSIVE
Tensile Strength (min) Yield Strength, at .5% extension under load min Elongation, in 2 in. or 50 mm min Brinell Hardness   Remarks
Ksi MPa Ksi MPa % typical BHN  
48 330 25 170 24    
SIZE RANGE: OVER 1"
Tensile Strength (min) Yield Strength, at .5% extension under load min Elongation, in 2 in. or 50 mm min Brinell Hardness   Remarks
Ksi MPa Ksi MPa % typical BHN  
46 315 20 140 28    

C26000
H02 Half-Hard Temper

SIZE RANGE: UNDER ½" DIAMETER
Tensile Strength (min) Yield Strength, at .5% extension under load min Elongation, in 2 in. or 50 mm min Brinell Hardness   Remarks
Ksi MPa Ksi MPa % typical BHN  
57 395 35 240 15    
SIZE RANGE: ½" DIAMETER TO 1" INCLUSIVE
Tensile Strength (min) Yield Strength, at .5% extension under load min Elongation, in 2 in. or 50 mm min Brinell Hardness   Remarks
Ksi MPa Ksi MPa % typical BHN  
54 370 32 220 20    
SIZE RANGE: OVER 1"
Tensile Strength (min) Yield Strength, at .5% extension under load min Elongation, in 2 in. or 50 mm min Brinell Hardness   Remarks
Ksi MPa Ksi MPa % typical BHN  
50 345 30 205 25    

C26000
H04 Hard Temper

SIZE RANGE: UNDER ½" DIAMETER
Tensile Strength (min) Yield Strength, at .5% extension under load min Elongation, in 2 in. or 50 mm min Brinell Hardness   Remarks
Ksi MPa Ksi MPa % typical BHN  
70 485 50 345 10    
SIZE RANGE: ½" DIAMETER TO 1" INCLUSIVE
Tensile Strength (min) Yield Strength, at .5% extension under load min Elongation, in 2 in. or 50 mm min Brinell Hardness   Remarks
Ksi MPa Ksi MPa % typical BHN  
65 450 45 310 15    
SIZE RANGE: OVER 1"
Tensile Strength (min) Yield Strength, at .5% extension under load min Elongation, in 2 in. or 50 mm min Brinell Hardness   Remarks
Ksi MPa Ksi MPa % typical BHN  
60 415 40 275 20    

Physical Properties (provided by CDA)

  US Customary Metric
Melting Point - Liquidus 1750° F 954° C
Melting Point - Solidus 1680° F 916° C
Density 0.308 lb/in3 at 68° F 8.53 gm/cm3 at 20° C
Specific Gravity 8.53 8.53
Electrical Conductivity 28% IACS at 68° F 0.162 MegaSiemens/cm at 20° C
Thermal Conductivity 70 Btu · ft/(hr · ft2 · °F) at 68° F 121.2 W/m at 20° C
Coefficient of Thermal Expansion 11.1 · 10-6 per °F (68°-572° F) 19.2 · 10-6 per °C (20°-300° C)
Specific Heat Capacity 0.09 Btu/lb/°F at 68° F 377.1 J/kg at 293° C
Modulus of Elasticity in Tension 16000 ksi 110317 MPa
Modulus of Rigidity 6000 ksi 41369 MPa

Fabrication Properties (provided by CDA)

Joining Technique Suitability
Soldering Excellent
Brazing Excellent
Oxyacetylene Welding Good
Gas Shielded Arc Welding Good
Coated Metal Arc Welding Not Recommended
Spot Weld Fair
Seam Weld Not Recommended
Butt Weld Good
Capacity for Being Cold Worked Excellent
Capacity for Being Hot Formed Fair

Thermal Properties (provided by CDA)

Treatment Temp./Time - US Temp./Time - SI
Stress Temperature  
Solution Minimum  
Solution Maximum  
Solution Time  
Solution Medium  
Precipitation Value  
Precipitation Time  
Precipitation Medium  
Annealing Minimum 800 427
Annealing Maximum 1400 760
Annealing Time  
Hot Works Minimum 1350 732
Hot Works Maximum 1550 843

FIND A PRODUCT

SEARCH BY
CDA NUMBER

REQUEST A QUOTE
C24000 C26000 C31600 C52100 C53400 C64210 C65100 C67600 C69400 C69430 C83600 C83800 C84200 C84400 C84800 C85700 C86200 C86400
C86500 C86700 C89320 C89325 C89520 C89831 C89833 C89844 C90500 C90700 C90800 C90810 C91000 C91100 C91300 C91600 C91700 C92200
C92300 C92500 C92700 C92800 C92900 C93400 C93500 C93600 C93700 C93800 C93900 C94000 C94100 C94300 C94700 C94700HT C94800 C95200
C95300 C95300HT C95400HT C95410 C95410HT C95500HT C95520HT C95600 C95800 C96400 C96900HT C97300 C97600 C97800 C99500 CONCAST380
C31400 C51000 C54400 C63000 C63020 C64200 C67300 C86300 C89835 C90300 C93200 C95400 C95500 C95510 C95900