Continuous Cast

Lead improves machinability in C923 leaded tin bronze but does not materially affect mechanical properties. This alloy is a free-cutting version of tin bronze, having similar properties and uses.

C92300 SPEC SHEET CONCAST LINE CARD

C92300

Product Description:. Leaded Tin Bronze
Solids: 1/2" to 13" O.D.
Tubes: 1" to 16" O.D.
Rectangles: Up to 20"
Standard Lengths: 144"
Shape/Form: semi-finished, mill stock or near-net shapes, anode, bar stock, billet/bloom, squares, hex, plate, profile or structural shape, flats/rectangular bar

Typical Uses

Builders Hardware: structural castings
Fasteners: nuts
Industrial: bearings, bushings, gears, high pressure hydraulic equipment, piston rings, pump impellers, pump parts, valve bodies
Plumbing: high-pressure steam equipment

Similar or Equivalent Specification

CDA ASTM SAE AMS Federal Military Other
C92300 B505
B505M
B143-2B		 621
J461
J462		   QQ-C-390, D3;
QQ-B-1005, Comp 6		 MIL-B-11553, Comp 6  

Chemical Composition

Cu%1 Pb% Sn% Zn% Fe% P% Ni%1,2 Al% S% Sb% Si%
Chemical Composition according to ASTM B505/B505M-18

1In determining Cu min., Cu may be calculated as Cu + Ni.   2Ni value includes Co.
Note: Cu + Sum of Named Elements, 99.3% min. Single values represent maximums.
85.00-
89.00		 0.30-
1.00		 7.50-
9.00		 2.50-
5.00		  
0.25		  
1.50		  
1.00		  
0.005		  
0.05		  
0.25		  
0.005

Machinability

Copper Alloy UNS No. Machinability Rating Density (lb/in3 at 68° F)
C92300 42 0.317

Mechanical Properties

Mechanical Properties according to ASTM B505/B505M-18
Tensile Strength, min Yield Strength, at 0.5% Extension Under Load, min Elongation, in 2 in. or 50 mm min Brinell Hardness (500 kg load) Remarks
ksi MPa ksi MPa % typical BHN  
40 276 19 131 16 70  

Physical Properties

Physical Properties provided by CDA
  US Customary Metric
Melting Point - Liquidus 1830 °F 999 °C
Melting Point - Solidus 1570 °F 854 °C
Density 0.317 lb/in3 at 68 °F 8.77 gm/cm3 at 20 °C
Specific Gravity 8.77 8.77
Electrical Conductivity 12% IACS at 68 °F 0.07 MegaSiemens/cm at 20 °C
Thermal Conductivity 43.2 Btu/sq ft/ft hr/°F at 68 °F 74.8 W/m at 20 °C
Coefficient of Thermal Expansion 68-392 10 · 10-6 per °F (68-392 °F) 17.3 · 10-6 per °C (20-200 °C)
Specific Heat Capacity 0.09 Btu/lb/°F at 68 °F 377.1 J/kg at 20 °C
Modulus of Elasticity in Tension 14000 ksi 96500 MPa
Incipient Melting 600 °F 316 °C

Fabrication Properties

Fabrication Properties provided by CDA

*Since brazing is performed within the hot-short range, strain must be avoided during brazing and cooling.
Technique Suitability
Soldering Excellent
Brazing* Good
Oxyacetylene Welding Not Recommended
Gas Shielded Arc Welding Not Recommended
Coated Metal Arc Welding Not Recommended
Machinability Rating 42

Thermal Properties

Thermal Properties provided by CDA

*Temperature is measured in Fahrenheit.   **For Stress Relief, Solution Treatment and Annealing - Time is measured in hours/inch of thickness. For Precipitation Heat Treatment - Time is measured in hours.
Treatment Value* Time**
Stress Relief 500  
Solution Treatment   0

FIND A PRODUCT

SEARCH BY
CDA NUMBER

REQUEST A QUOTE
C14500 C23000 C24000 C26000 C31400 C31600 C46400 C51000 C52100 C53400 C54400 C62400 C63000 C63020 C64200 C64210 C65100 C67300 C67400 C67410 C67600 C69300 C69400 C69430 C72900 (AMS 4596) C72900 (AMS 4597)
C72900 (AMS 4598) C83600 C83800 C84200 C84400 C84800 C85700 C86200 C86300 C86400 C86500 C86700 C87850 C89320 C89325 C89520 C89831 C89833 C89835 C89844 C90300 C90500 C90700
C90800 C91000 C91100 C91300 C91600 C91700 C92200 C92300 C92500 C92700 C92800 C92900 C93200 C93400 C93500 C93600 C93700 C93800 C93900 C94000 C94100 C94300 C94700
C94700HT C94800 C95200 C95300 C95300HT C95400 C95400HT C95410 C95410HT C95500 C95500HT C95510 C95520HT C95600 C95800 C95900 C96400 C96900HT C97300 C97600 C97800 C99500 CONCAST380
✖

Bezoek https://anabolensteroiden.com/ voor een uitgebreide selectie van betrouwbare anabolen. Haal het maximale uit je training en spiergroei.