C94100

REFERENCE
GUIDE

Continuous Cast

The lead content in high-leaded tin bronze alloys is between 7 percent and 30 percent. This group of alloys is free cutting and retains favorable thermal conductivity and good lubricity due to the presence of lead. High-leaded tin bronzes are ideal for bearing applications where there could be a loss of the lubrication boundary. These alloys perform extremely well in unforgiving environments where foreign matter may be present, such as dirt and other foreign materials. They are able to envelope foreign matter due to their malleable nature and, in doing so, protect the wear surface of a coupled part.

C94100

Product Description: High-Leaded Tin Bronze
Solids: 1/2" to 10" O.D.
Tubes: 1" to 16" O.D.*
Rectangles: Up to 10"
Standard Lengths: 144"
Shape/Form: semi-finished, mill stock or near-net shapes, anode, bar stock, billet/bloom, squares, hex, plate, profile or structural shape, flats/rectangular bar

 *Consult mill for wall thickness

Typical Uses

Industrial: thrust block

Similar or Equivalent Specification

CDA ASTM SAE AMS Federal Military Other
C94100 B505
B505M
    QQ-C-390, E5 MIL-B-16261, Grade X  

Chemical Composition

Cu% Pb% Sn% Zn% Fe% P% Ni%1 Al% S%2 Sb% Si%
Chemical Composition according to ASTM B505/B505M-18

1Ni value includes Co.   2For continuous castings, S shall be 0.25% max.
Note: Cu + Sum of Named Elements, 98.7% min. Single values represent maximums.
72.00-
79.00
18.00-
22.00
4.50-
6.50
 
1.00
 
0.25
 
1.50
 
1.00
 
0.005
 
0.25
 
0.80
 
0.005

Machinability

Copper Alloy UNS No. Machinability Rating Density (lb/in3 at 68 °F)
C94100 80 0.336

Mechanical Properties

Mechanical Properties according to ASTM B505/B505M-18
Tensile Strength, min Yield Strength, at 0.5% Extension Under Load, min Elongation, in 2 in. or 50 mm min Brinell Hardness (500 kg load) Remarks
ksi MPa ksi MPa % typical BHN  
25 172 17 117 7 50  