C69430

ALLOY SEARCH MODULE

GET STARTED
SEARCH CLEAR

SPECIFICATION CROSS-REFERENCE CHART

Info

Product Description: Silicon Red Brass
Tempers: H04 Hard
Solids: 3/8" to 2" O.D.
Hex: 3/8" to 2" O.D.
Rectangles: Consult Mill
Standard Lengths: 144"

Typical Uses

Industrial: valve stems

Similar or Equivalent Specification

CDA ASTM ASARCON SAE AMS Federal Military Other
C69430 B371
B371M
           

Chemical Composition

Cu%1 Pb% Zn% Fe% Si% As%
Chemical Composition according to ASTM B371/B371M-15

1Cu value includes Ag.
Note: Cu + Sum of Named Elements, 99.5% min. Single values represent maximums.
80.00-
83.00
 
0.30
 
Rem.
 
0.20
3.50-
4.50
0.03-
0.06

Machinability

Copper Alloy UNS No. Machinability Rating Density (lb/in3 at 68 °F)
C69430 30 0.260

Mechanical Properties

Mechanical Properties according to ASTM B371/B371M-15

C69430

H04 Hard

SIZE RANGE: UP TO 1" INCLUSIVE
Tensile Strength, min Yield Strength, at .5% Extension Under Load, min Elongation, in 4x Diameter or Thickness of Specimen, min Rockwell "B" Hardness   Remarks
ksi MPa ksi MPa % typical HRB  
80 550 40 276 15 95  
SIZE RANGE: OVER 1" TO 2" INCLUSIVE
Tensile Strength, min Yield Strength, at .5% Extension Under Load, min Elongation, in 4x Diameter or Thickness of Specimen, min Rockwell "B" Hardness   Remarks
ksi MPa ksi MPa % typical HRB  
75 515 35 241 15 95  
SIZE RANGE: OVER 2"
Tensile Strength, min Yield Strength, at .5% Extension Under Load, min Elongation, in 4x Diameter or Thickness of Specimen, min Rockwell "B" Hardness   Remarks
ksi MPa ksi MPa % typical HRB  
65 450 35 241 15 95  

Physical Properties

Physical Properties provided by CDA
  US Customary Metric
Melting Point - Liquidus 1685 °F 918 °C
Melting Point - Solidus 1510 °F 821 °C
Density 0.26 lb/in3 at 68 °F 7.19 gm/cm3 at 20 °C
Specific Gravity 7.19 7.19
Electrical Conductivity 6.2% IACS at 68 °F 0.04 MegaSiemens/cm at 20 °C
Thermal Conductivity 15 Btu/sq ft/ft hr/°F at 68 °F 25.98 W/m at 20 °C
Coefficient of Thermal Expansion 68-572 11.2 · 10-6 per °F (68-572 °F) 19.3 · 10-6 per °C (20-300 °C)
Specific Heat Capacity 0.09 Btu/lb/°F at 68 °F 377.1 J/kg at 293 °C
Modulus of Elasticity in Tension 16000 ksi 110310 MPa

Fabrication Properties

Fabrication Properties provided by CDA
Joining Technique Suitability
Soldering Excellent
Brazing Excellent
Oxyacetylene Welding Good
Spot Weld Good
Seam Weld Good
Butt Weld Good
Capacity for Being Cold Worked Good
Capacity for Being Hot Formed Excellent