Tough and corrosion resistant, C67300 manganese bronze, also known as C673, is a high-tensile bronze ideal for high-load, low-speed applications that require a combination of outstanding wear characteristics and high bearing strength.

C67300 spec sheet C67300 size schedule C67300 brochure Weight calculator Standard products

C67300

Product description: Manganese bronze
Tempers: H02 half hard
Solids: 3/4" to 3" O.D.
Hex: Consult Mill
Standard lengths: 144"

Typical uses

Fasteners: fasteners, lead screw nuts
Industrial: bearings, bearings (pins) bushings, clutch bearings, drive shafts, gears and cams, idler pins, piston heads, propeller shafts, pump parts, seal rings, shaft bushings, sleeve bearings, spindles, thrust bearings, wear plates
Marine: hardware, valve seats
Other: connecting rods

Similar or equivalent specification

CDA ASTM SAE AMS Federal Military Other
C67300   J461
J463 		       

Chemical composition

Cu% Pb% Sn% Zn% Fe% Ni%1 Al% Mn% Si%
Chemical composition according to SAE J463
1Ni value includes Co.
Note: Single values represent maximums.
58.00-
63.00		 0.40-
3.00		  
0.30		  
Rem.		  
0.50		  
0.25		  
0.25		 2.00-
3.50		 0.50-
1.50

Machinability

Copper alloy UNS No. Machinability rating Density (lb/in3 at 68 °F)
C67300 70 0.300

Mechanical properties

Mechanical properties according to SAE J463

C67300

H02 half hard

Size range: up to 1" inclusive
Tensile strength, min Yield strength, at 0.5% extension under load,, min Elongation, in 4x Diameter or Specimen Thickness, min Rockwell "B" hardness Remarks
ksi MPa ksi MPa % min HRB  
65 448 40 276 12 70
Size range: over 1" to 3" inclusive
Tensile strength, min Yield strength, at 0.5% extension under load,, min Elongation, in 4x Diameter or Specimen Thickness, min Rockwell "B" hardness Remarks
ksi MPa ksi MPa % min HRB  
58 400 35 241 15 70
Size range: over 3"
Tensile strength, min Yield strength, at 0.5% extension under load,, min Elongation, in 4x Diameter or Specimen Thickness, min Rockwell "B" hardness Remarks
ksi MPa ksi MPa % min HRB  
55 380 30 205 18 65

Physical properties

Physical properties provided by CDA
  US Customary Metric
Melting point - liquidus 1605 °F 874 °C
Density 0.3 lb/in3 at 68 °F 8.3 gm/cm3 at 20 °C
Specific gravity 8.3 8.3
Electrical conductivity 22% IACS at 68 °F 0.13 MegaSiemens/cm at 20 °C
Thermal conductivity 55 Btu/sq ft/ft hr/°F at 68 °F 95 W/m at 20 °C
Coefficient of thermal expansion 68-572 11 · 10-6 per °F (68-572 °F) 19 · 10-6 per °C (20-300 °C)
Modulus of elasticity in tension 17000 ksi 117212 MPa

Fabrication properties

Fabrication properties provided by CDA
Technique Suitability
Machinability rating 70

Common fabrication processes

Hot forging and pressing, machining

Common fabrication processes provided by CDA

Find a product

Search by
CDA number

Request a quote
C14500 C23000 C24000 C26000 C31400 C31600 C46400 C51000 C52100 C53400 C54400 C62400 C63000 C63020 C64200 C64210 C65100 C67300 C67400 C67410 C67600 C69300 C69400 C69430 C72900 (AMS 4596) C72900 (AMS 4597)
C72900 (AMS 4598) C83600 C83800 C84200 C84400 C84800 C85700 C86200 C86300 C86400 C86500 C86700 C87850 C89320 C89325 C89520 C89831 C89833 C89835 C89844 C90300 C90500 C90700
C90800 C91000 C91100 C91300 C91600 C91700 C92200 C92300 C92500 C92700 C92800 C92900 C93200 C93400 C93500 C93600 C93700 C93800 C93900 C94000 C94100 C94300 C94700
C94700HT C94800 C95200 C95300 C95300HT C95400 C95400HT C95410 C95410HT C95500 C95500HT C95510 C95520HT C95600 C95800 C95900 C96400 C96900HT C97300 C97600 C97800 C99500 CONCAST380
✖